TITANLENE ® LDF265YZ Low density
polyethylene
Material Notes : Low density polyethylene for extrusion film.
Applications :
● Heavy duty sacks
● Shrink film
● Construction film
Additives : Barefoot
Advantages :
● Excellent mechanical
properties
● Good process ability
Information provided by Titan Chemicals
Physical Properties |
Metric |
English |
Comments |
Base Resin Density |
0.922 g/cc |
0.0333 ib/in³ |
ASTM D1505 |
Thickness |
150 microns |
5.91 mil |
Extruded at 1.5:1 BUR |
Base Resin Melt Index |
0.330 g/10 min |
0.330 g/10 min |
ASTM D1238 |
|
|
|
|
Mechanical Properties |
Metric |
English |
Comments |
Film Elongation at Break, MD |
490 % |
490 % |
ASTM D882 |
Film Elongation at Break, TD |
620 % |
620 % |
ASTM D882 |
Dart Drop |
4.00 g/micron |
102 g/mil |
ASTM D1709 |
Film Tensile Strength at Break, MD |
21.6 MPa |
3130 psi |
ASTM D882 |
Film Tensile Strength at Break, TD |
19.6 MPa |
2840 psi |
ASTM D882 |
1% Secant Modulus, MD |
176.52 MPa |
25602 psi |
ASTM D882 |
1% Secant Modulus, TD |
196.14 MPa |
28447 psi |
ASTM D882 |
|
|
|
|
Thermal Properties |
Metric |
English |
Comments |
Vicat Softening Point |
97.0 °C |
207 °F |
Resin; ASTM D1525 |
|
|
|
|
Processing Properties |
Metric |
English |
Comments |
Melt Temperature |
160 – 190 °C |
320 – 374 °F |
|
Blow-up Ratio (BUR) |
|
1.50 |
|
|
|
|
|
Descriptive Properties |
|
|
|
Trouser tear, MD g/micron |
|
9 |
ASTM D1938 |
Trouser tear, TD g/micron |
|
8.5 |
ASTM D1938 |